Quantitative comparison of the water permeable zone among four types of dental adhesives used with a dual-cured composite

Juhea Chang, Jeffrey Platt, Keewook Yi, Michael A. Cochran

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

This study compared silver penetration in the adhesive interface among four versions of adhesives from the same manufacturer: OptiBond FL, OptiBond Solo Plus, OptiBond Solo Plus Dual Cure, and OptiBond Solo Plus Self-Etch, when coupled with dual-cured composite, CoreRestore 2 (Kerr). Twenty flat dentin surfaces were prepared using one of the adhesives and bonded with the composite, following the manufacturer's instructions. The surfaces were sectioned into 2-mm slabs and immersed in ammoniacal silver nitrate for 24 hours. Each specimen was exposed to a photodeveloping solution for eight hours and examined with a scanning electron microscope (SEM). The water permeable area occupied by the silver nitrate tracer was determined, and the relative weight of silver was analyzed by wavelength dispersive spectrometry (WDS). The OptiBond FL group had a significantly lower silver content than the other groups (p

Original languageEnglish (US)
Pages (from-to)346-353
Number of pages8
JournalOperative Dentistry
Volume31
Issue number3
StatePublished - May 2006

Fingerprint

Dental Cements
Silver
Adhesives
Silver Nitrate
Water
Dentin
Spectrum Analysis
Electrons
Weights and Measures
OptiBond FL
OptiBond Solo Plus

ASJC Scopus subject areas

  • Dentistry(all)

Cite this

Quantitative comparison of the water permeable zone among four types of dental adhesives used with a dual-cured composite. / Chang, Juhea; Platt, Jeffrey; Yi, Keewook; Cochran, Michael A.

In: Operative Dentistry, Vol. 31, No. 3, 05.2006, p. 346-353.

Research output: Contribution to journalArticle

@article{9006165026e2456f9f908e018a8d54b6,
title = "Quantitative comparison of the water permeable zone among four types of dental adhesives used with a dual-cured composite",
abstract = "This study compared silver penetration in the adhesive interface among four versions of adhesives from the same manufacturer: OptiBond FL, OptiBond Solo Plus, OptiBond Solo Plus Dual Cure, and OptiBond Solo Plus Self-Etch, when coupled with dual-cured composite, CoreRestore 2 (Kerr). Twenty flat dentin surfaces were prepared using one of the adhesives and bonded with the composite, following the manufacturer's instructions. The surfaces were sectioned into 2-mm slabs and immersed in ammoniacal silver nitrate for 24 hours. Each specimen was exposed to a photodeveloping solution for eight hours and examined with a scanning electron microscope (SEM). The water permeable area occupied by the silver nitrate tracer was determined, and the relative weight of silver was analyzed by wavelength dispersive spectrometry (WDS). The OptiBond FL group had a significantly lower silver content than the other groups (p",
author = "Juhea Chang and Jeffrey Platt and Keewook Yi and Cochran, {Michael A.}",
year = "2006",
month = "5",
language = "English (US)",
volume = "31",
pages = "346--353",
journal = "Operative Dentistry",
issn = "0361-7734",
publisher = "Indiana University School of Dentistry",
number = "3",

}

TY - JOUR

T1 - Quantitative comparison of the water permeable zone among four types of dental adhesives used with a dual-cured composite

AU - Chang, Juhea

AU - Platt, Jeffrey

AU - Yi, Keewook

AU - Cochran, Michael A.

PY - 2006/5

Y1 - 2006/5

N2 - This study compared silver penetration in the adhesive interface among four versions of adhesives from the same manufacturer: OptiBond FL, OptiBond Solo Plus, OptiBond Solo Plus Dual Cure, and OptiBond Solo Plus Self-Etch, when coupled with dual-cured composite, CoreRestore 2 (Kerr). Twenty flat dentin surfaces were prepared using one of the adhesives and bonded with the composite, following the manufacturer's instructions. The surfaces were sectioned into 2-mm slabs and immersed in ammoniacal silver nitrate for 24 hours. Each specimen was exposed to a photodeveloping solution for eight hours and examined with a scanning electron microscope (SEM). The water permeable area occupied by the silver nitrate tracer was determined, and the relative weight of silver was analyzed by wavelength dispersive spectrometry (WDS). The OptiBond FL group had a significantly lower silver content than the other groups (p

AB - This study compared silver penetration in the adhesive interface among four versions of adhesives from the same manufacturer: OptiBond FL, OptiBond Solo Plus, OptiBond Solo Plus Dual Cure, and OptiBond Solo Plus Self-Etch, when coupled with dual-cured composite, CoreRestore 2 (Kerr). Twenty flat dentin surfaces were prepared using one of the adhesives and bonded with the composite, following the manufacturer's instructions. The surfaces were sectioned into 2-mm slabs and immersed in ammoniacal silver nitrate for 24 hours. Each specimen was exposed to a photodeveloping solution for eight hours and examined with a scanning electron microscope (SEM). The water permeable area occupied by the silver nitrate tracer was determined, and the relative weight of silver was analyzed by wavelength dispersive spectrometry (WDS). The OptiBond FL group had a significantly lower silver content than the other groups (p

UR - http://www.scopus.com/inward/record.url?scp=33745465839&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33745465839&partnerID=8YFLogxK

M3 - Article

C2 - 16802643

AN - SCOPUS:33745465839

VL - 31

SP - 346

EP - 353

JO - Operative Dentistry

JF - Operative Dentistry

SN - 0361-7734

IS - 3

ER -